Optimization and Efficiency Enhancement of Modified Polymer Solar Cells.

In this study, an organic bulk heterojunction (BHJ) solar cell with a spiro OMeTAD as a hole transport layer (HTL) and a PDINO as an electron transport layer (ETL) was simulated through the one-dimensional solar capacitance simulator (SCAPS-1D) software to examine the performance of this type of organic polymer thin-film solar cell. As an active layer, a blend of polymer donor PBDB-T and non-fullerene acceptor ITIC-OE was used. Numerical simulation was performed by varying the thickness of the HTL and the active layer. Firstly, the HTL layer thickness was optimized to 50 nm; after that, the active-layer thickness was varied up to 80 nm. The results of these simulations demonstrated that the HTL thickness has rather little impact on efficiency while the active-layer thickness improves efficiency significantly. The temperature effect on the performance of the solar cells was considered by simulations performed for temperatures from 300 to 400 K; the efficiency of the solar cell decreased with increasing temperature. Generally, polymer films are usually full of traps and defects; the density of the defect (N t ) value was also introduced to the simulation, and it was confirmed that with the increase in defect density (N t ), the efficiency of the solar cell decreases. After thickness, temperature and defect density optimization, a reflective coating was also applied to the cell. It turned out that by introducing the reflective coating to the back side of the solar cell, the efficiency increased by 2.5%. Additionally, the positive effects of HTL and ETL doping on the efficiency of this type of solar cells were demonstrated.