Simulating porcelain firing effect on the structure, corrosion and mechanical properties of Co-Cr-Mo dental alloy fabricated by soft milling.
Angeliki G LekatouSevasti EmmanouilidouKonstantinos DimitriadisMaria BaikousiMichael A KarakassidesSimeon AgathopoulosPublished in: Odontology (2023)
This study aims at evaluating the effect of simulating porcelain firing on the microstructure, corrosion behavior and mechanical properties of a Co-Cr-Mo alloy fabricated by Metal Soft Milling (MSM). Two groups of Co-28Cr-5Mo specimens (25 × 20 × 3 mm) were prepared by MSM: The as-sintered (AS) specimens and the post-fired (PF) specimens that were subjected to 5 simulating porcelain firing cycles without applying the ceramic mass onto their surface. Phase identification by X-ray Diffraction (XRD), microstructure examination by optical microscopy and Scanning Electron Microscopy combined with Energy-Dispersive X-ray Spectroscopy (SEM/EDX), corrosion testing by cyclic polarization and chronoamperometry in simulated body fluid (SBF), the latter test accompanied by Cr 3+ and Cr 6+ detection in the electrolyte through the 1.5-diphenylcarbazide (DPC) method and UV/visible spectrophotometry, and mechanical testing by micro-/nano-indentation were conducted to evaluate the effect of the post-firing cycles on the properties of Co-Cr-Mo. The results were statistically analyzed by the t test (p < 0.05: statistically significant). All specimens had a mixed γ-fcc and ε-hcp cobalt-based microstructure with a dispersion of pores filled with SiO 2 and a fine M 23 C 6 intergranular presence. PF led to an increase in the ε-Co content and slight grain coarsening. Both AS and PF alloys showed high resistance to general and localized corrosion, whereas neither Cr 6+ nor Cr 3+ were detected during the passivity-breakdown stage. PF improved the mechanical properties of the AS-alloy, especially the indentation modulus and true hardness (statistically significant differences: p = 0.0009 and 0.006, respectively). MSM and MSM/simulating-porcelain firing have been proven trustworthy fabrication methods of Co-Cr-Mo substrates for metal-ceramic prostheses. Moreover, the post-firing cycles improve the mechanical behavior of Co-Cr-Mo, which is vital under the dynamically changing loads in the oral cavity, whereas they do not degrade the corrosion performance.