Synthesis, Properties, and Application of Ultrathin and Flexible Tellurium Nanorope Films: Beyond Conventional 2D Materials.

Nanomaterials that can be easily processed into thin films are highly desirable for their wide range of applicability in electrical and optical devices. Currently, Te-based 2D materials are of interest because of their superior electrical properties compared to transition metal dichalcogenide materials. However, the large-scale manufacturing of these materials is challenging, impeding their commercialization. This paper reports on ultrathin, large-scale, and highly flexible Te and Te-metal nanorope films grown via low-power radiofrequency sputtering for a short period at 25 °C. Additionally, the feasibility of such films as transistor channels and flexible transparent conductive electrodes is discussed. A 20 nm thick Te-Ni-nanorope-channel-based transistor exhibits a high mobility (≈450 cm 2 V -1 s -1 ) and on/off ratio (10 5 ), while 7 nm thick Te-W nanorope electrodes exhibit an extremely low haze (1.7%) and sheet resistance (30 Ω sq -1 ), and high transmittance (86.4%), work function (≈4.9 eV), and flexibility. Blue organic light-emitting diodes with 7 nm Te-W anodes exhibit significantly higher external quantum efficiencies (15.7%), lower turn-on voltages (3.2 V), and higher and more uniform viewing angles than indium-tin-oxide-based devices. The excellent mechanical flexibility and easy coating capability offered by Te nanoropes demonstrate their superiority over conventional nanomaterials and provide an effective outlet for multifunctional devices.