Synthesis and investigation of sulfonated poly( p -phenylene)-based ionomers with precisely controlled ion exchange capacity for use as polymer electrolyte membranes.

To achieve precise control of sulfonated polymer structures, a series of poly( p -phenylene)-based ionomers with well-controlled ion exchange capacities (IECs) were synthesised via a three-step technique: (1) preceding sulfonation of the monomer with a protecting group, (2) nickel(0) catalysed coupling polymerisation, and (3) cleavage of the protecting group of the polymers. 2,2-Dimethylpropyl-4-[4-(2,5-dichlorobenzoyl)phenoxy]benzenesulfonate (NS-DPBP) was synthesised as the preceding sulfonated monomer by treatment with chlorosulfuric acid and neopentyl alcohol. NS-DPBP was readily soluble in various organic solvents and stable during the nickel(0) catalysed coupling reaction. Sulfonated poly(4-phenoxybenzoyl-1,4-phenylene) (S-PPBP) homopolymer and seven types of random copolymers (S-PPBP- co -PPBP) with different IECs were obtained by varying the stoichiometry of NS-DPBP. The IECs and weight average molecular weights ( M w s) of ionomers were in the range of 0.41-2.84 meq. g -1 and 143 000-465 000 g mol -1 , respectively. The water uptake, proton conductivities, and water diffusion properties of ionomers exhibited a strong IEC dependence. Upon increasing the IEC of S-PPBP- co -PPBPs from 0.86 to 2.40 meq. g -1 , the conductivities increased from 6.9 × 10 -6 S cm -1 to 1.8 × 10 -1 S cm -1 at 90% RH. S-PPBP and S-PPBP- co -PPBP (4 : 1) with IEC values >2.40 meq. g -1 exhibited fast water diffusion (1.6 × 10 -11 to 8.0 × 10 -10 m 2 s -1 ), and were comparable to commercial perfluorosulfuric acid polymers. When fully hydrated, the maximum power density and the limiting current density of membrane electrode assemblies (MEAs) prepared with S-PPBP- co -PPBP (4 : 1) were 712 mW cm -2 and 1840 mA cm -2 , respectively.