Ultrahigh Ferroelectric and Piezoelectric Properties in BiFeO 3 -BaTiO 3 Epitaxial Films Near Morphotropic Phase Boundary.

Ferroelectric solid solutions with composition near the morphotropic phase boundary (MPB) have gained extensive attention recently due to their excellent ferroelectric and piezoelectric properties. Here, we have demonstrated a strategy to realize the controllable preparation of BiFeO 3 -BaTiO 3 (BF-BT) epitaxial films near the MPB. A series of high-quality BF-BT films were fabricated by pulsed laser deposition via adjusting oxygen partial pressure (PO 2 ) using a BF-BT ceramic target. A continuous transition from rhombohedral to tetragonal phase was observed upon increasing PO 2 . Particularly, the film with a pure tetragonal phase exhibited a large remnant polarization of ∼90.6 μC/cm 2 , while excellent piezoelectric performance with an ultrahigh strain (∼0.48%) was obtained in the film with coexisting rhombohedral and tetragonal phases. The excellent ferroelectric and piezoelectric properties endow the BF-BT system near the MPB with great application prospects in lead-free electronic devices.