Concentration Optimization of Localized Cu 0 and Cu + on Cu-Based Electrodes for Improving Electrochemical Generation of Ethanol from Carbon Dioxide.

Copper-based electrodes can catalyze electroreduction of CO 2 to two-carbon products. However, obtaining a specific product with high efficiency depends on the oxidation state of Cu for the Cu-based materials. In this study, Cu-based electrodes were prepared on fluorinated tin oxide (FTO) using the one-step electrodeposition method. These electrodes were used as efficient electrocatalysts for CO 2 reduction to ethanol. The concentration ratio of Cu 0 and Cu + on the electrodes was precisely modulated by adding monoethanolamine (MEA). The results of spectroscopic characterization showed that the concentration ratio of localized Cu + and Cu 0 (Cu + /Cu 0 ) on the Cu-based electrodes was controlled from 1.24/1 to 1.54/1 by regulating the amount of MEA. It was found that the electrode exhibited the best electrochemical efficiency and ethanol production in the CO 2 reduction reaction at the optimal concentration ratio Cu + /Cu 0 of 1.42/1. The maximum faradaic efficiencies of ethanol and C 2 were 48% and 77%, respectively, at the potential of -0.6 V vs. a reversible hydrogen electrode (RHE). Furthermore, the optimal concentration ratio of Cu + /Cu 0 achieved the balance between Cu + and Cu 0 with the most favorable free energy for the formation of *CO intermediate. The stable existence of the *CO intermediate significantly contributed to the formation of the C-C bond for ethanol production.