Unlocking High-Current Performance in Silicon Anode: Synergistic Phosphorus Doping and Nitrogen-Doped Carbon Encapsulation to Enhance Lithium Diffusivity.

The silicon (Si) offers enormous theoretical capacity as a lithium-ion battery (LIB) anode. However, the low charge mobility in Si particles hinders its application for high current loading. In this study, ball-milled phosphorus-doped Si nanoparticles encapsulated with nitrogen-doped carbon (P-Si@N-C) are employed as an anode for LIBs. P-doped Si nanoparticles are first obtained via ball-milling and calcination of Si with phosphoric acid. N-doped carbon encapsulation is then introduced via carbonization of the surfactant-assisted polymerization of pyrrole monomer on P-doped Si. While P dopant is required to support the stability at high current density, the encapsulation of Si particles with N-doped carbon is influential in enhancing the overall Li + diffusivity of the Si anode. The combined approaches improve the anode's Li + diffusivity up to tenfold compared to the untreated anode. It leads to exceptional anode stability at a high current, retaining 87 % of its initial capacity under a large current rate of 4000 mA g -1 . The full-cell comprising P-Si@N-C anode and LiFePO 4 cathode demonstrates 94 % capacity retention of its initial capacity after 100 cycles at 1 C. This study explores the effective strategies to improve Li + diffusivity for high-rate Si-based anode.