Recyclable Fe/S co-doped nanocarbon derived from metal-organic framework as a peroxymonosulfate activator for efficient removal of 2,4-dichlorophenol.
Yu DuanYujie LiuYun WangHongyong WangWentao YinGang XuPublished in: Environmental science and pollution research international (2022)
In this study, a recyclable Fe/S co-doped nanocarbon (Fe/S-NC) was successfully prepared by the pyrolysis of ZIF-8 confined with Fe(II) and added S. Characterization showed that a highly graphitized carbon-based material co-doped with sulfur and iron was successfully prepared. This Fe/S-NC can efficiently activate PMS to remove organic pollutants in water. The effect of different synthesis conditions on the degradation efficiency of 2,4-DCP was studied by orthogonal experiments. The optimized Fe/S-NC/PMS system exhibited excellent catalytic performance and could degrade more than 99.7% of 2,4-DCP within 30 min. Even after 5 cycles, the degradation efficiency could still be maintained above 96.3%, which proved that the catalytic system had good cycle performance. In addition, the effect of pH on catalytic performance showed that the degradation rate of 2,4-DCP exceeds 96.7% in the pH range of groundwater (pH = 5-9). We had confirmed that the free radicals that caused 2,4-DCP degradation were SO 4 ·- , ·OH, O 2 ·- , and 1 O 2 , which played important roles in degrading organic pollutants. These research results show that the Fe/S-NC/PMS system can be used as an efficient, stable, and environmentally friendly system to treat organic pollutants in groundwater.