Design, Synthesis and Properties of Semi-Alicyclic Colorless and Transparent Polyimide Films with High Glass Transition Temperatures and Low Retardation for Potential Applications in Flexible Electronics.

Polyimide (PI) optical films with high glass transition temperatures (high-T g ), high optical transparency, and low optical retardations (low-R th ) are highly desired in advanced optoelectronic applications. However, the standard PI films usually suffer from deep colors, high optical anisotropies and limited T g values. In the current work, a series of semi-alicyclic colorless and transparent PI (CPI) films were developed from hydrogenated pyromellitic dianhydride stereoisomers, 1S,2R,4S,5R-hydrogenated pyromellitic dianhydride and 1R,2S,4S,5R-hydrogenated pyromellitic dianhydride, and fluorene-containing diamines, including 9,9-bis(4-aminophenyl)fluorene and 9,9-bis(3-fluoro-4-aminophenyl)fluorene, respectively. The derived CPI films showed T g values higher than 420 °C according to differential scanning calorimetry measurements. In addition, the fluorene-based CPI film showed optical transmittances higher than 80% at the wavelength of 400 nm, with yellow indices in the range of 0.60~1.01 and haze values below 3.0%. The CPI films showed average refractive indices from 1.5407 to 1.6309, extremely low birefringence at the level of minus fourth power of ten, and further exhibited quite low optical retardations below 10 nm.