Ultrasensitive and bifunctional ZnO nanoplates for an oxidative electrochemical and chemical sensor of NO 2 : implications towards environmental monitoring of the nitrite reaction.

Shivsharan M MaliParag P ChavanYuvraj H NavaleVikas B PatilBhaskar R Sathe
Published in: RSC advances (2018)
Herein, we focused on the one pot synthesis of ZnO nanoplates (NP edge thickness of ∼100 nm) using a chemical emulsion approach for chemical (direct) and electrochemical (indirect) determination of NO 2 . The structural and morphological elucidation of the as-synthesized ZnO NPs was carried out by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive analysis of X-ray (EDAX), thermogravimetric analysis (TGA) and BET-surface area measurements. The XRD studies of the as-synthesised NPs reveal that ZnO NPs have a Wurtzite type crystal structure with a crystallite size of ∼100 nm. Such ZnO NPs were found to be highly sensitive to NO 2 gas at an operating temperature of 200 °C. Electrocatalytic abilities of these ZnO NPs towards NO 2 /NO 2 - were verified through cyclic voltammetry (CV) and linear sweep voltammetry (LSV) using aqueous 1 mM NO 2 - (nitrite) in phosphate buffer (pH 7) solution. The results revealed enhanced activity at an onset potential of 0.60 V vs. RCE, achieved at a current density of 0.14 mA cm -2 . These ZnO NPs show selective NO 2 detection in the presence of other reactive species including CO, SO 2 , CH 3 OH and Cl 2 . These obtained results show that this chemical route is a low cost and promising method for ZnO NPs synthesis and recommend further exploration into its applicability towards tunable electrochemical as well as solid state gas sensing of other toxic gases.
Keyphrases