Study on the Properties of FEVE Modified with Ag 2 O/OH-MWCNTS Nanocomposites for Use as Adhesives for Wooden Heritage Objects.

The durability of wooden heritage objects and sites can be affected by external environmental factors, leading to decay, cracking, and other forms of deterioration, which might ultimately result in significant and irreversible loss. In this study, a FEVE resin was modified with Ag 2 O/OH-MWCNTS (MA), denoted as MAF, where three concentrations were prepared using in situ precipitation, and the resulting composite adhesive was characterized by a high viscosity and effective bacteriostatic properties, demonstrating a better viscosity and thermal stability, as well as antibacterial properties, than pure FEVE resin. The results show that MAF adhesives present good thermal stability, as evidenced by a lower mass loss rate following treatment at 800 °C compared to the pure FEVE resin. At a consistent shear rate, the viscosity of MAF demonstrates a notable increase with the proportion of MA, which is better than that of FEVE. This suggests that the nano-Ag 2 O particles in MA act as physical crosslinking agents in FEVE, improving the viscosity of the composite adhesive MAF. The adhesion strength between MAF and wood exhibits a similar trend, with wooden samples showing higher shear strengths as the proportion of MA increases in comparison to FEVE. Simultaneously, the antibacterial effects of the MAF adhesive exceeded 1 mm for Trichoderma , Aspergillus niger , and white rot fungi . The antibacterial activity of the MAF adhesive exhibited a direct correlation with the concentration of Ag 2 O/OH-MWCNTS, with the most pronounced inhibitory effect observed on Trichoderma. The MAF adhesive demonstrates promising prospects as an adhesive for wooden heritage artifacts, offering a novel approach for the rapid, environmentally friendly, and efficient development of composite adhesives with superior adhesive properties.