Carbonaceous-Material-Induced Gelation of Concentrated Electrolyte Solutions for Application in Lithium-Sulfur Battery Cathodes.

Lithium-sulfur (Li-S) batteries can theoretically deliver high energy densities exceeding 2500 Wh kg -1 . However, high sulfur loading and lean electrolyte conditions are two major requirements to enhance the actual energy density of the Li-S batteries. Herein, the use of carbon-dispersed highly concentrated electrolyte (HCE) gels with sparingly solvating characteristics as sulfur hosts in Li-S batteries is proposed as a unique approach to construct continuous electron-transport and ion-conduction paths in sulfur cathodes as well as achieve high energy density under lean-electrolyte conditions. The sol-gel behavior of carbon-dispersed sulfolane-based HCEs was investigated using phase diagrams. The sol-to-gel transition was mainly dependent on the amount of the carbonaceous material and the Li salt content. The gelation was caused by the carbonaceous-material-induced formation of an integrated network. Density functional theory (DFT) calculations revealed that the strong cation-π interactions between Li + and the induced dipole of graphitic carbon were responsible for facilitating the dispersion of the carbonaceous material into the HCEs, thereby permitting gel formation at high Li-salt concentrations. The as-prepared carbon-dispersed sulfolane-based composite gels were employed as efficient sulfur hosts in Li-S batteries. The use of gel-type sulfur hosts eliminates the requirement for excess electrolytes and thus facilitates the practical realization of Li-S batteries under lean-electrolyte conditions. A Li-S pouch cell that achieved a high cell-energy density (up to 253 Wh kg -1 ) at a high sulfur loading (4.1 mg cm -2 ) and low electrolyte/sulfur ratio (4.2 μL mg -1 ) was developed. Furthermore, a Li-S polymer battery was fabricated by combining the composite gel cathode and a polymer gel electrolyte.