Role of temperature on bio-printability of gelatin methacrylate bioinks in two-step cross-linking strategy for tissue engineering applications.

Biofabrication of tissue constructs using additive manufacturing has shown promising results in reconstructing three-dimensional (3D) living tissues for various applications, including tissue engineering, regenerative medicine, drug discovery, and high-throughput drug screening. In extrusion-based bioprinters, stable formation of filaments and high-fidelity deposition of bioinks are the primary challenges in fabrication of physiologically relevant tissue constructs. Among various bioinks, gelatin methacryloyl (GelMA) is known as a photocurable and physicochemically tunable hydrogel with a demonstrated biocompatibility and tunable biodegradation properties. The two-step crosslinking of GelMA (reversible thermal gelation and permanent photo-crosslinking) has attracted researchers to make complex tissue constructs. Despite promising results in filament formation and printability of this hydrogel, the effect of temperature on physicochemical properties, cytocompatibility, and biodegradation of the hydrogel are to be investigated. This work studies the effect of thermoreversible, physical crosslinking on printability of GelMA. The results of 3D printing of GelMA at different temperatures followed by irreversible chemical photo-crosslinking show that the decrease in temperature improves the filament formation and shape fidelity of the deposited hydrogel, particularly at the temperatures around 15 °C. Time dependant mechanical testing of the printed samples revealed that decreasing the extruding temperature increases the elastic properties of the extruded filaments. Furthermore, our novel approach in minimizing the slippage effect during rheological study enabled to measure changes in linear and nonlinear viscoelastic properties of the printed samples at different temperatures. A considerable increase in storage modulus of the extruded samples printed at lower temperatures confirms their higher solid behavior. Scanning electron microscopy revealed a remarkable decrease in porosity of the extruded hydrogels by decreasing the temperature. Chemical analysis by Fourier-transform infrared spectroscopy (FTIR) and circular dichroism (CD) showed a direct relationship between the coil-helix transition in hydrogel macromers and its physical alterations. Finally, biodegradation and cytocompatibility of the extruded hydrogels decreased at lower extruding temperatures.