Feasibility and Characterization Mortar Blended with High-Amount Basic Oxygen Furnace Slag.

Wei-Ting LinChia-Jung TsaiJie ChenWeidong Liu
Published in: Materials (Basel, Switzerland) (2018)
Basic oxygen furnace slag (BOFS) was ground to three levels of fineness as a replacement for cement at weight proportions of 10, 30, 50, and 70 wt.%. Fineness and weight proportion were shown to have significant effects on the flowability and setting time of the mortars. The expansion of BOFS mortars increased with an increase in the proportion of cement replaced, thereby exacerbating the effects of cracking. Optimal mechanical properties were achieved when 10 wt.% of the cement was replaced using BOFS with fineness of 10,000 cm²/g. The compressive strength of BOFS mortar is similar to that of ordinary Portland mortar, which makes BOFS suitable for the partial replacement of cement as a supplementary cementitious material. Scanning electron microscopy results revealed that the reaction of CaO with H₂O results in the formation of C⁻S⁻H colloids, whereas the reaction of SiO₂ with Al₂O₃ produces C⁻A⁻S⁻H colloids. The use of BOFS as a partial replacement for Portland cement could make a tremendous contribution to the steel industry and help to lower CO₂ emissions.
Keyphrases
  • electron microscopy
  • body mass index
  • physical activity
  • weight loss
  • weight gain
  • high resolution
  • mass spectrometry
  • risk assessment
  • magnetic nanoparticles
  • anaerobic digestion