Improvement of Fermi-Level Pinning and Contact Resistivity in Ti/Ge Contact Using Carbon Implantation.

Effects of carbon implantation (C-imp) on the contact characteristics of Ti/Ge contact were investigated. The C-imp into Ti/Ge system was developed to reduce severe Fermi-level pinning (FLP) and to improve the thermal stability of Ti/Ge contact. The current density ( J )-voltage ( V ) characteristics showed that the rectifying behavior of Ti/Ge contact into an Ohmic-like behavior with C-imp. The lowering of Schottky barrier height (SBH) indicated that the C-imp could mitigate FLP. In addition, it allows a lower specific contact resistivity ( ρ c ) at the rapid thermal annealing (RTA) temperatures in a range of 450-600 °C. A secondary ion mass spectrometry (SIMS) showed that C-imp facilitates the dopant segregation at the interface. In addition, transmission electron microscopy (TEM) and electron energy loss spectroscopy (EELS) mapping showed that after RTA at 600 °C, C-imp enhances the diffusion of Ge atoms into Ti layer at the interface of Ti/Ge. Thus, carbon implantation into Ge substrate can effectively reduce FLP and improve contact characteristics.