A PEDOT based graft copolymer with enhanced electronic stability.

Poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) remains the most investigated conjugated polymer in bioelectronics, due to its biocompatibility, high conductivity, and commercial availability. Despite these advantages, it suffers from structural and electronic instability, associated with the PSS component. Here, a graft copolymer based on ionised sulfonic modified PEDOT, poly(EDOTS- g -EDOT), was electrochemically synthesised with demonstrated structural and electronic stability and enhanced electrochemical performance. The graft copolymer was insoluble in water without crosslinking, and exhibited enhanced ion diffusion upon electrochemical switching, as revealed by its volumetric capacitance (159 ± 8 F cm -3 ), which was significantly higher than that of spin-coated PEDOT:PSS films (41 ± 5 F cm -3 ). Similarly, its performance as an active channel material in organic electrochemical transistors (OECTs) was superior to the spin-coated PEDOT:PSS, as shown for instance by its high normalised transconductance (273 ± 79 S cm -1 ) and a significantly high I ON / I OFF ratio (19 345 ± 1205). Its short- and long-term electronic stability were also confirmed with no drop in its output drain current, despite its high swelling degree. In contrast, the spin-coated PEDOT:PSS experienced a significant deterioration in its performance over the same operational time. The facile synthesis and improved performance of poly(EDOTS- g -EDOT) highlight the importance of innovative material design in overcoming existing operational shortcomings in electronic devices.