Single Iridium Atom Doped Ni2P Catalyst for Optimal Oxygen Evolution.
Qi WangZhe ZhangChao CaiMaoyu WangZhi Liang ZhaoMenghao LiXiang HuangShaobo HanHua ZhouZhenxing FengLei LiJun LiHu XuJoseph S FranciscoM Danny GuPublished in: Journal of the American Chemical Society (2021)
Single-atom catalysts (SACs) with 100% active sites have excellent prospects for application in the oxygen evolution reaction (OER). However, further enhancement of the catalytic activity for OER is quite challenging, particularly for the development of stable SACs with overpotentials <180 mV. Here, we report an iridium single atom on Ni2P catalyst (IrSA-Ni2P) with a record low overpotential of 149 mV at a current density of 10 mA·cm-2 in 1.0 M KOH. The IrSA-Ni2P catalyst delivers a current density up to ∼28-fold higher than that of the widely used IrO2 at 1.53 V vs RHE. Both the experimental results and computational simulations indicate that Ir single atoms preferentially occupy Ni sites on the top surface. The reconstructed Ir-O-P/Ni-O-P bonding environment plays a vital role for optimal adsorption and desorption of the OER intermediate species, which leads to marked enhancement of the OER activity. Additionally, the dynamic "top-down" evolution of the specific structure of the Ni@Ir particles is responsible for the robust single-atom structure and, thus, the stability property. This IrSA-Ni2P catalyst offers novel prospects for simplifying decoration strategies and further enhancing OER performance.