Effect of Ceramic Thickness on the Bond Strength to Resin-Luting Agents before and after Thermal Cycling.

Carolina Rodrigues de SouzaJúlio César Lemos DuarteLincoln Pires Sousa BorgesAnalia Gabriella Borges FerrazRafael Leonardo Xediek ConsaniRafael Rocha PachecoAmérico Bortolazzo CorrerLourenço Correr-Sobrinho
Published in: Brazilian dental journal (2024)
This study investigated microshear bond strength (µSBS) of two (2) dual-cured resin-luting agents (RelyX™ Ultimate and RelyX™ U200) when photoactivated through varying thicknesses of lithium disilicate, with or without thermal cycling. Discs of IPS e.max Press of 0.5, 1.5, and 2 mm in thickness were obtained. Elastomer molds (3.0 mm in thickness) with four cylinder-shaped orifices 1.0 mm in diameter, were placed onto the ceramic surfaces and filled with resin-luting agents. A Mylar strip, glass plate, and load of 250 grams were placed over the filled mold. The load was removed and the resin-luting agents were photoactivated through the ceramics using a single-peak LED (Radii Plus.) All samples were stored in distilled water at 37oC for 24 h. Half of the samples were subjected to thermal cycling (3,000 cycles; 5ºC and 55ºC). All samples were then submitted to µSBS test using a universal testing machine (Instron 4411) at a crosshead speed of 0.5 mm/min. Data were submitted to three-way ANOVA and Tukey post-hoc test (α=0.05). The mean µSBS at 24 h was significantly higher than after thermal cycling (p<0.05). No statistical difference was found between resin-luting agents (p > 0.05). The mean µSBS for groups photoactivated through 0.5 mm ceramic were significantly higher than 1.5 mm and 2.0 mm (p < 0.05). In conclusion, increased ceramic thicknesses reduced the bond strength of tested resin-luting agents to lithium disilicate. No differences were found between resin-luting agents. Thermal cycling reduced the bond strength of both resin-luting agents.
Keyphrases
  • high intensity
  • optical coherence tomography
  • escherichia coli
  • electronic health record
  • ionic liquid
  • atomic force microscopy
  • solid state