Boosting ORR Catalytic Activity by Integrating Pyridine-N Dopants, a High Degree of Graphitization, and Hierarchical Pores into a MOF-Derived N-Doped Carbon in a Tandem Synthesis.

N-doped carbon materials represent promising metal-free electrocatalysts for the oxygen reduction reaction (ORR), the cathode reaction in fuel cells, metal-air batteries, and so on. A challenge for optimizing the ORR catalytic activities of these electrocatalysts is to tune their local structures and chemical compositions in a rational and controlled way that can achieve the synergistic function of each factor. Herein, we report a tandem synthetic strategy that integrates multiple contributing factors into an N-doped carbon. With an N-containing MOF (ZIF-8) as the precursor, carbonization at higher temperatures leads to a higher degree of graphitization. Subsequent NH3 etching of this highly graphitic carbon enabled the introduction of a higher content of pyridine-N sites and higher porosity. By optimizing these three factors, the resultant carbon materials displayed ORR activity that was far superior to that of carbon derived from a one-step pyrolysis. The onset potential of 0.955 V versus a reversible hydrogen electrode (RHE) and the half-wave potential of 0.835 V versus RHE are among the top ranks of metal-free ORR catalysts and are comparable to commercial Pt/C (20 wt %) catalysts. Kinetic studies revealed lower H2 O2 yields, higher electron-transfer numbers, and lower Tafel slopes for these carbon materials compared with that derived from a one-step carbonization. These findings verify the effectiveness of this tandem synthetic strategy to enhance the ORR activity of N-doped carbon materials.