Polymer-Magnetic Composite Particles of Fe₃O₄/Poly(o-anisidine) and Their Suspension Characteristics under Applied Magnetic Fields.

Fe₃O₄/poly(o-anisidine) (POA) magnetic composite nanoparticles with their core-shell structure were synthesized by chemical oxidation polymerization technique and adopted as a magneto-responsive magnetorheological (MR) material. The chemical structure and morphology of core-shell nanoparticles were identified by FT-IR, SEM, TEM, and elemental analyzer. Pycnometer and vibrating sample magnetometer showed that the magnetic saturation and density of the Fe₃O₄/POA particles were reduced by the POA shell coatings. The rheological properties of the MR suspension dispersed in a silicone oil at various magnetic field strengths were investigated using a rotating rheometer under a magnetic field. The resulting MR suspension showed a typical Newtonian fluid behavior in the absence of external stimuli. When an external magnetic field was applied, it formed a strong chain structure, acting like a solid with a yield stress. Further solid-like behaviors were observed from storage shear relaxation and viscoelastic tests. Finally, the Fe₃O₄/POA nanoparticles showed better dispersion stability than pure Fe₃O₄ nanoparticles with 50% improvement.