Functionality Selection Principle for High Voltage Lithium-ion Battery Electrolyte Additives.
Chi-Cheung SuMeinan HeCameron PeeblesLi ZengAdam TornheimChen LiaoLu ZhangJie WangYan WangZhengcheng ZhangPublished in: ACS applied materials & interfaces (2017)
A new class of electrolyte additives based on cyclic fluorinated phosphate esters was rationally designed and identified as being able to stabilize the surface of a LiNi0.5Mn0.3Co0.2O2 (NMC532) cathode when cycled at potentials higher than 4.6 V vs Li+/Li. Cyclic fluorinated phosphates were designed to incorporate functionalities of various existing additives to maximize their utilization. The synthesis and characterization of these new additives are described and their electrochemical performance in a NMC532/graphite cell cycled between 4.6 and 3.0 V are investigated. With 1.0 wt % 2-(2,2,2-trifluoroethoxy)-1,3,2-dioxaphospholane 2-oxide (TFEOP) in the conventional electrolyte the NMC532/graphite cell exhibited much improved capacity retention compared to that without any additive. The additive is believed to form a passivation layer on the surface of the cathode via a sacrificial polymerization reaction as evidenced by X-ray photoelectron spectroscopy (XPS) and nuclear magnetic resonsance (NMR) analysis results. The rational pathway of a cathode-electrolyte-interface formation was proposed for this type of additive. Both experimental results and the mechanism hypothesis suggest the effectiveness of the additive stems from both the polymerizable cyclic ring and the electron-withdrawing fluorinated alkyl group in the phosphate molecular structure. The successful development of cyclic fluorinated phosphate additives demonstrated that this new functionality selection principle, by incorporating useful functionalities of various additives into one molecule, is an effective approach for the development of new additives.
Keyphrases