Research on the Strengthening Advantages on Using Cellulose Nanofibers as Polyvinyl Alcohol Reinforcement.

Quim TarrèsHelena Oliver-OrtegaManuel AlcalàFrancesc Xavier EspinachPere MutjéMarc Delgado-Aguilar
Published in: Polymers (2020)
The present work aims to combine the unique properties of cellulose nanofibers (CNF) with polyvinyl alcohol (PVA) to obtain high-performance nanocomposites. CNF were obtained by means of TEMPO-mediated ((2,2,6,6-Tetramethylpiperidin-1-yl)oxyl) oxidation, incorporated into the PVA matrix by means of compounding in a single-screw co-rotating internal mixer and then processed by means of injection molding. It was found that CNF were able to improve the tensile strength of PVA in 85% when 4.50 wt % of CNF were added. In addition, the incorporation of a 2.25 wt % of CNF enhanced the tensile strength to the same level that when 40 wt % of microsized fibers (stone groundwood pulp, SGW) were incorporated, which indicated that CNF possessed significantly higher intrinsic mechanical properties than microsized fibers. SGW was selected as reference for microsized fibers due to their extended use in wood plastic composites. Finally, a micromechanical analysis was performed, obtaining coupling factors near to 0.2, indicating good interphase between CNF and PVA. Overall, it was found that the use of CNF is clearly advantageous to the use of common cellulosic fibers if superior mechanical properties are desired, but there are still some limitations that are related to processing that restrict the reinforcement content at low contents.
Keyphrases
  • aqueous solution