Yb Substitution and Ultralow Thermal Conductivity of the Ca 3- x Yb x AlSb 3 (0 ≤ x ≤ 0.81(1)) System.

A series of Yb-substituted Zintl phases in the Ca 3- x Yb x AlSb 3 (0 ≤ x ≤ 0.81(1)) system has been synthesized by initial arc melting and post-heat treatment, and their isotypic crystal structures were characterized by both powder and single crystal X-ray diffraction analysis. All four title compounds adopted the Ca 3 AlAs 3 -type structure (space group Pnma , Pearson code oP 28, Z = 4). The overall structure can be described as a combination of the 1-dimensional (1D) infinite chain of ∞ 1 [Al(Sb 2 Sb 2/2 )] formed by two vertices sharing [AlSb 4 ] tetrahedral moieties and three Ca 2+ /Yb 2+ mixed sites located in between these 1D chains. The charge balance and the resultant independency of the 1D chains in the title system were explained by the Zintl-Klemm formalism [Ca 2+ /Yb 2+ ] 3 [(4b-Al 1- )(1b-Sb 2- ) 2 (2b-Sb 1- ) 2/2 ]. A series of DFT calculations proved that (1) the band overlap between the d -orbital states from two types of cations and the p -orbital states from Sb at the high symmetry Γ point implied a heavily doped degenerate semiconducting behavior of the quaternary Ca 2 YbAlSb 3 model and (2) the site preference of Yb for the M1 site was due to the electronic-factor criterion based on the Q values of each atomic site. The electron localization function calculations also proved that the two different shapes of lone pairs of the Sb atoms─the "umbrella-shape" and the "C-shape"─are determined by local geometry and the coordination environment on the anionic frameworks. Thermoelectric measurements of the quaternary title compound Ca 2.19(1) Yb 0.81 AlSb 3 showed an approximately two times larger ZT value than that of ternary Ca 3 AlSb 3 at 623 K due to increased electrical conductivity and ultralow thermal conductivity originated from Yb substitution for Ca.