Three-dimensional printing of poly(glycerol sebacate fumarate) gadodiamide-poly(ethylene glycol) diacrylate structures and characterization of mechanical properties for soft tissue applications.
Prashanth RaviJamie WrightPanos S ShiakolasTré R WelchPublished in: Journal of biomedical materials research. Part B, Applied biomaterials (2018)
Bioresorbable materials have been frequently used to three-dimensional (3D) print biomedical structures. In this study, we developed a technique to 3D print poly(glycerol sebacate fumarate) gadodiamide (Rylar)-poly(ethylene glycol) diacrylate (PEGDA) samples and investigated their mechanical and thermal properties as a function of (PS) and ultraviolet intensity (UVI). The Young's modulus (E), ultimate tensile strength (UTS), failure strain (ɛF ), and glass transition temperature (Tg ) showed strong correlation with PS and UVI. Results showed E to be between 1.31 and 3.12 MPa, UTS between 0.07 and 0.43 MPa, and ɛF between 7 and 20% with brittle failure. The Tg was observed to lie between -54.48 and -49.10 ° C without secondary/tertiary transitions. Dominant elastic behavior was observed from the dynamic mechanical testing viscoelastic data. Testing results were used to develop a regression predictive model for E as a function of PS and UVI. The model performance was evaluated experimentally with an average absolute error of 3.62%. The E and stress-strain response of our 3D printed samples show agreement with published data for human tracheal cartilage, and the mechanical properties were comparable to other published soft polymeric scaffolds/patches. The E' moduli were also similar to bovine articular cartilage. We have successfully demonstrated that Rylar, a novel bioresorbable radiopaque polymer, when blended with PEGDA can be 3D printed controllably for soft tissue applications such as airway obstructions. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 107B: 664-671, 2019.