The Effect of B 4 C Powder on Properties of the WAAM 2319 Al Alloy.

With ER2319 and B 4 C powder as feedstocks and additives, respectively, a wire arc additive manufacturing (WAAM) system based on double-pulse melting electrode inert gas shielded welding (DP-MIG) was used to fabricate single-pass multilayer 2319 aluminum alloy. The results showed that, compared with additive manufacturing component without B 4 C, the addition of which can effectively reduce the grain size (from 43 μm to 25 μm) of the tissue in the deposited layer area and improve its mechanical properties (from 231 MPa to 286 MPa). Meanwhile, the mechanical properties are better in the transverse than in the longitudinal direction. Moreover, the strengthening mechanism of B 4 C on the mechanical properties of aluminum alloy additive manufacturing mainly includes dispersion strengthening from fine and uniform B 4 C granular reinforcing phases and fine grain strengthening from the grain refinement of B 4 C. These findings shed light on the B 4 C induced grain refinement mechanism and improvement of WAAM 2319 Al alloy.