Selectively Nitrogen Doped ALD-IGZO TFTs with Extremely High Mobility and Reliability.

Achieving high mobility and reliability in atomic layer deposition (ALD)-based IGZO thin-film transistors (TFTs) with an amorphous phase is vital for practical applications in relevant fields. Here, we suggest a method to effectively increase stability while maintaining high mobility by employing the selective application of nitrous oxide plasma reactant during plasma-enhanced ALD (PEALD) at 200 °C process temperature. The nitrogen-doping mechanism is highly dependent on the intrinsic carbon impurities or nature of each cation, as demonstrated by a combination of theoretical and experimental research. The Ga 2 O 3 subgap states are especially dependent on plasma reactants. Based on these insights, we can obtain high-performance indium-rich PEALD-IGZO TFTs (threshold voltage: -0.47 V; field-effect mobility: 106.5 cm 2 /(V s); subthreshold swing: 113.5 mV/decade; hysteresis: 0.05 V). In addition, the device shows minimal threshold voltage shifts of +0.45 and -0.10 V under harsh positive/negative bias temperature stress environments (field stress: ±2 MV/cm; temperature stress: 95 °C) after 10000 s.