A Comparative Study on the Aerobic Biodegradation of the Biopolymer Blends of Poly(butylene succinate), Poly(butylene adipate terephthalate) and Poly(lactic acid).
Nomvuyo NomadoloOmotola Esther DadaAndri SwanepoelTeboho Clement MokhenaSudhakar MuniyasamyPublished in: Polymers (2022)
The aim of the present work is to evaluate the rate and mechanisms of the aerobic biodegradation of biopolymer blends under controlled composting conditions using the CO 2 evolution respirometric method. The biopolymer blends of poly (butylene adipate terephthalate) (PBAT) blended with poly (lactic acid) (PLA), and PBAT blended with poly (butylene succinate) (PBS) by melt extrusion, were tested to evaluate the amount of carbon mineralized under home and industrial composting conditions. The changes in the structural, chemical, thermal and morphological characteristics of the biopolymer blends before and after biodegradation were investigated by FT-IR, DSC, TGA, XRD and SEM. Both blends showed higher degradation rates under industrial composting conditions, when compared to home composting conditions. This was confirmed by FT-IR analysis showing an increase in the intensity of hydroxyl and carbonyl absorption bands. SEM revealed that there was microbial colony formation and disintegration on the surfaces of the biopolymer blends. The obtained results suggest that industrial composting conditions are the most suitable for an enhanced biodegradation of the biopolymer blends viz PBAT-PBS and PBAT-PLA.