Marginal Discrepancies of Monolithic Zirconia Crowns: The Influence of Preparation Designs and Sintering Techniques.

There was a significant interaction between finish line widths, crown thickness, and sintering protocol on the marginal gaps in both sintering protocols; 1.0 mm finish line preparations with either 0.8 mm or 1.5 mm occlusal reduction had better marginal fit in both sintering protocols compared to 0.5 mm or 1.2 mm finish lines. Smaller marginal discrepancies were observed for standard sintering crowns with a 0.5 mm finish line and 1.5 mm occlusal reduction. Conservative occlusal reduction should be accompanied with a 1.2 mm finish line to obtain better marginal fit for full-contoured zirconia crowns.