High-Barrier, Biodegradable Films with Polyvinyl Alcohol/Polylactic Acid + Wax Double Coatings: Influence of Relative Humidity on Transport Properties and Suitability for Modified Atmosphere Packaging Applications.

Polyvinyl alcohol (PVOH) exhibits outstanding gas-barrier properties, which favor its use as a biodegradable, high-barrier coating on food-packaging films, possibly in combination with modified atmospheres. Nonetheless, its high sensitivity to water can result in a severe loss of barrier properties, significantly limiting its applications with fresh foods and in high-humidity conditions. In this work, the water vapor (P WV ) and oxygen permeability (PO 2 ) of high-barrier biodegradable films with PVOH/PLA + wax double coatings were extensively characterized in a wide range of relative humidity (from 30 to 90%), aimed at understanding the extent of the interaction of water with the wax and the polymer matrices and the impact of this on the permeation process. What is more, a mathematical model was applied to the P WV data set in order to assess its potential to predict the permeability of the multilayer films by varying storage/working relative humidity (RH) conditions. The carbon dioxide permeability (PCO 2 ) of the films was further evaluated, and the corresponding permselectivity values were calculated. The study was finally augmented through modified atmosphere packaging (MAP) tests, which were carried out on double-coated films loaded with 0 and 5% wax, and UV-Vis analyses. The results pointed out the efficacy of the PLA + wax coating layer in hampering the permeation of water molecules, thus reducing PVOH swelling, as well as the UV-shielding ability of the multilayer structures. Moreover, the MAP tests underlined the suitability of the double-coated films for being used as a sustainable alternative for the preservation of foods under modified atmospheres.