Ionic Liquid Catalysis in Cyclic Carbonate Synthesis for the Development of Soybean Oil-Based Non-Isocyanate Polyurethane Foams.

A method for obtaining non-isocyanate polyurethane (NIPU) foams from cyclic carbonate (CC) based on soybean oil was developed. For this purpose, cyclic carbonate was synthesized from epoxidized soybean oil and CO 2 using various ionic liquids (ILs) as catalysts. Among the tested ILs, the highest selectivity (100%) and CC yield (98%) were achieved for 1-ethyl-3-methylimidazolium ([emim]Br). Without any purification, the resulting cyclic carbonate was reacted directly with diethylenetriamine as a model crosslinking agent to produce NIPU foams. It was found that the soybean oil-based CC synthesized with bromide imidazolium ionic liquids exhibited significantly shorter gelling times (8 min 50 s for [emim]Br and 9 min 35 s for [bmim]Br) compared to those obtained with the conventional TBAB catalyst (26 min 15 s). A shorter gelling time is a crucial parameter for the crosslinking process in foams. The obtained foams were subjected to mechanical tests and a morphology analysis.