Evaluating the pH of Various Commercially Available Beverages in Pakistan: Impact of Highly Acidic Beverages on the Surface Hardness and Weight Loss of Human Teeth.

Naresh KumarFaiza AminDanya HashemSara KhanHuma ZaidiSehrish RahmanTooba FarhanSyed Junaid MahmoodMuhammad Asif AsgharMuhammad Sohail Zafar
Published in: Biomimetics (Basel, Switzerland) (2022)
The objectives of this study were to investigate the pH of common beverages and to evaluate the effects of common acidic beverages on the surface hardness and weight loss of human tooth specimens. A total of 106 beverages were conveniently purchased from supermarkets in Karachi, Pakistan. Prior to evaluation, beverages were refrigerated or stored at room temperature in accordance with the manufacturers' recommendations. Beverages were categorized into six groups: 'Sports and Energy drinks', 'Water', 'Fruit Juices and Drinks', 'Sodas', 'Milk and Flavored Milk' and 'Teas and Coffee'. Using a pH meter, the pH of each beverage was measured in triplicate at room temperature. In addition, the influence of five highly acidic beverages on the weight loss and surface hardness of human tooth specimens was evaluated using gravimetric analysis and the Vickers hardness tester, respectively. 'Sports and Energy drinks', 'Fruits Juices and Drinks' and 'Sodas' were the most acidic beverage categories, with a pH range of 3.00-5.00. A total of 33% of beverages tested in this study were highly acidic (pH less than 4.00), 29% of beverages were moderately acidic (pH 4.00-4.99) and 31% were mildly acidic (pH 5.00-6.99). Significant weight loss was observed in all immersed specimens compared to control counterparts ( p < 0.05). Similarly, for surface hardness, five highly acidic beverages (Red Bull, Pepsi, Apple Cidra, Tang Mosambi and Tang Orange) significantly decreased the surface hardness of specimens ( p < 0.05). The pH levels of commonly available beverages in Pakistan are highly acidic, which may encourage loss of minerals from teeth; hence, affecting their surface hardness.
Keyphrases