The Effect of UV Treatment on Surface Contact Angle, Fibroblast Cytotoxicity, and Proliferation with Two Types of Zirconia-Based Ceramics.

UV photofunctionalization of Zirconia-based materials for abutment fabrication is a promising approach that might influence the formation of a sound peri-implant seal, thus promoting long-term soft and hard tissue implant integration. This study aimed to evaluate the effect of UV treatment of test specimens made by two different ZnO 2 -based ceramic materials on the hydrophilicity, cell cytotoxicity, and proliferation of human gingival fibroblasts (HGFs). Two Zirconia-based materials, high-translucent and ultra-translucent multi-layered Zirconia (Katana, Kuraray Noritake, Japan), were used to prepare a total of 40 specimens distributed in two equally sized groups based on the material ( n = 20). The same surface finishing protocol was applied for all specimens, as suggested by the manufacturer. Half the specimens from each group were treated with UV-C light for 48 h. Water contact angle (WCA), fibroblast cytotoxicity, and proliferation were investigated. The WCA values for the high-translucent Zirconia ranged from 69.9° ± 6.4° to 73.7° ± 13.9° for the treated/non-treated specimens and from 79.5° ± 12.8° to 83.4° ± 11.4° for the ultra-translucent multi-layered Zirconia, respectively. However, the difference was insignificant (F(16) = 3.50, p = 0.292). No significant difference was observed for the fibroblast cytotoxicity test. The results for proliferation revealed a significant difference, which was material-dependent (F(8) = 9.58, p = 0.005). We found that UV surface photofunctionalization of ZrO 2 -based materials alters the human gingival fibroblast cell viability, which might produce favourable results for cell proliferation.